Super Fine Powder NanoX of Better Corrosion than Hastelloy 1000℃ Temperature
Abrasion or Erosion for Small ID HVOF Spraying, Coated Ground Tube
1. AMTmetalTech Patent Amorphous + Nanocrystalline Super Fine Powder NanoX of Better Corrosion than Hastelloy 1000℃ Temperature Abrasion or Erosion for Small ID Tube HVOF Spraying
HVAF or HVOF Applications
Ferro Amorphous + Nanocrystalline
Better corrosion resist than 316L. Good Erosion except Strong Acid or Alkali. Good Abrasion Resist, High Hardness HV700-900. Temperature Resist under 500℃. Low Cost.
ID under 80mm.
ID above 80mm or HVAF Flash Ferro Amorphous Powder.
Nickel Amorphous + Nanocrystalline
Better corrosion resist than Hastelloy C276 and In625. Super Erosion and Good Abrasion Resist even for pure Acid or Alkali. High Hardness HV700-900. Temperature Resist up to 1000℃.
ID under 80mm.
ID above 80mm or HVAF Flash Hard Hastelloy.
AMTmetalTech quantity produces Patent gas atomized Amorphous + Nanocrystalline Ferro powder NanoA for tube Inside ID HVOF or HVAF thermal spraying coating is better corrosion resist than 316L, can resist various erosion except strong acid and alkali, and anti-temperature to 400℃.
AMTmetalTech Patent gas atomized Amorphous + Nanocrystalline Nickel alloy powder NanoX for tube Inside ID HVOF or HVAF thermal spraying coating is better corrosion or erosion than Hastelloy C276 and In625, can resist pure acid and alkali, anti-temperature up to 1000℃ replacing Nickel Clad Tube.
The coating hardness of both NanoA and NanoX is HV700-900.
Super Fine powder 2-10um is for spraying ID max. 80mm. 8-25um powder is for spraying ID above 80mm.
The coating is very Smooth at roughness Ra under 3um. The cost is competitive.
2. AMTmetalTech Long Small ID HVOF Sprayed and Ground Tube of Better Corrosion than Hastelloy 1000℃ Temperature Abrasion or Erosion Resist Replace Nickel Clad Tube
AMTmetalTech the world top quality equipment for long small tube Inside ID HVOF spraying can make the smallest Tube Inside diameter ID 60mm, the longest tube 4 meters. The Tube Inside roughness after Sraying and Grinding can be Ra 0.01-0.1um.
Please send us email to export@AMTmetalTech.com about Nickel Amorphous HVAF or HVOF Tube Inside ID Spraying Fine Atomized Powder Better Corrosion risist than Hastelloy C276 / Inconel In625 / Stellite of severe Erosion, Cavitation, high temperature Abrasion resist; Duplex Stainless Steel Powder for Binder Jet Printing / Speed Laser / PTA cladding / Plasma weld overlaying Replacing Chrome Plating for Coated Cylinders / Pistons / Roller / Screw Rotors / Valve / Stirrer Blade / Hydro Turbine Runner; Tungsten Carbide Hardmetal Cemented Clad Mud Pump Liner / Pipe / Sleeve / Glass Mold and Super Wear Plate; PDC Diffusion Bonding, Diamond Bearing etc.