FerroTiC Laser Cladding Powder
What is the Alternative Powder Substitutes or Replacements for Tungsten Carbide hardfacing Deposit or Weld Overlay Cladding?
AMTmetalTech is the supplier manufacturing Unique FerroTiC Titanium Carbide Alloy powder for super wear abrasion resist PTA Plasma or Laser Cladding Conical Mining Bits, Steel Rolling Guider, Mud Pump Liner, Auto Gas Valve, Hydro Turbine Runner etc.
Unique FerroTiC Titanium Carbide Hardface Deposit Powder Substitute Nickel Tungsten Carbide Laser / PTA Plasma Overlay Cladding or Cored Wire Filler of Wear, Corrosion, Cavitation Resist
11 
1. AMTmetalTech Unique Top Quality World Low Price FerroTiC Titanium Carbide Hardface Deposit Powders Replace Nickel Tungsten Carbide Laser / PTA Plasma Overlay Cladding or Cored Wire Filler Specifications
Tungsten Carbide is always the best for Super Wear or Abrasion and Impact Resistance. Titanium Carbide Alloy never can be the same Wear or Abrasion and Impact Resistance as Tungsten Carbide. When you need extreme super Wear or Abrasion and Impact Resistance regardless cost, please still use Tungsten Carbide. When you need not extreme super Wear or Abrasion and Impact Resistance meanwhile require competitive cost, our Unique Titanium Carbide Alloy can be the best choice for replacing the Tungsten Carbide in more than 10 times saving Cost against Performance or Working Life.
In the following table TxxFyy, xx means TiC volume rate while yy means matrix HRC hardness. F means Ferro Matrix. N means Nickel Matrix.
Type | TiC, V% | HRC | Cr+ Ni | Mn+Si | C+B+Mo | Fe | Density g/Cm3 | Corrosion Resist | Temperature Resist | Character & Applications |
T43N45 | 41-45 | 43-47 | 57-59 | 1.5-2.5 | 1.5-2.5 | ≤7 | ≈ 7.1 | Close to NiSiB | ≤ 1000℃ | Nickel Matrix Replace Cast Tungsten Carbide 60%W2C/WC-40%Ni45A |
T35N45 | 33-37 | 43-47 | 64-66 | 2.0-3.0 | 1.5-2.5 | ≤7 | ≈ 7.4 | Close to NiSiB | ≤ 1000℃ | Nickel Matrix Replace Cast Tungsten Carbide 52%W2C/WC-48%Ni45A |
T15N60 | 13-17 | 58-62 | 77-79 | 3.0-4.0 | 3.0-4.0 | ≤7 | ≈ 7.8 | Close to NiSiB | ≤ 1000℃ | Nickel Matrix Replace Cast Tungsten Carbide 25%W2C/WC-75%Ni60A |
T79KN45 | 77-81 | 43-47 | 18-20 | 0.5-1.5 | 0.3-1.3 | ≤10 | ≈ 5.9 | Close to NiSiB | ≤ 1000℃ | Ni45A Matrix Replace Cast Tungsten Carbide W2C/WC |
T79KN60 | 77-81 | 58-62 | 18-20 | 0.5-1.5 | 0.3-1.3 | ≤10 | ≈ 5.9 | Close to NiSiB | ≤ 1000℃ | Ni60A Matrix Replace Cast Tungsten Carbide W2C/WC |
T43F45 | 41-45 | 43-47 | 13.5-15.5 | 0.5-1.5 | 0.5-1.5 | 47-52 | ≈ 6.8 | Close to 316 | ≤ 550℃ | Fe45 Matrix Substitute Fused Tungsten Carbide 60%W2C/WC-40%Ni45A |
T35F45 | 33-37 | 43-47 | 15-17 | 0.5-1.5 | 0.5-1.5 | 54-58 | ≈ 7.0 | Close to 316 | ≤ 550℃ | Fe45 Matrix Substitute Fused Tungsten Carbide 52%W2C/WC-48%Ni45A |
T15F60 | 13-17 | 58-62 | 15.5-17.5 | 0.5-1.5 | 1.0-2.0 | 68-72 | ≈ 7.4 | Close to 316 | ≤ 550℃ | Fe60 Matrix Substitute Fused Tungsten Carbide 25%W2C/WC-75%Ni60A |
T43E43 | 41-45 | 41-45 | 36-40 | 1.5-2.5 | 4.0-6.0 | 20-24 | ≈ 6.8 | Better than 316L | ≤ 900℃ | Ferro Matrix Substitute Fused Tungsten Carbide 60%W2C/WC-40%Ni45A ≤ 900℃ Resist |
T35C40 | 33-37 | 38-42 | 32-36 | 1.5-2.5 | ≤2 | 37-41 | ≈ 7.0 | Better than 316L | ≤ 550℃ | Super Cavitation Abrasion Resist |
T79F20 | 77-81 | 18-22 | 4.0-8.0 | ≤1.5 | ≤1.5 | 22-26 | ≈ 5.8 | Close to 316 | ≤ 900℃ | Ferro Matrix Substitute Fused Tungsten Carbide W2C/WC |
T79KF42 | 77-81 | 40-44 | 4.0-8.0 | ≤1.5 | ≤1.5 | 22-26 | ≈ 5.8 | Close to 316 | ≤ 900℃ | Fe42 Matrix Substitute Fused Tungsten Carbide W2C/WC |
T79KF58 | 77-81 | 56-60 | 4.0-8.0 | ≤1.5 | ≤1.5 | 22-26 | ≈ 5.8 | Close to 316 | ≤ 900℃ | Fe58 Matrix Substitute Fused Tungsten Carbide W2C/WC |
2. AMTmetalTech Unique Top Quality World Low Price FerroTiC Titanium Carbide Hardmetal Powders Replace Nickel Tungsten Carbide Laser / PTA Plasma Overlay Cladding or Cored Wire Filler Production
AMTmetalTech unique FerroTiC Powder is the pure TiC clad with Super Steel to avoid the headache of pure TiC oxidizing and not easy to be wet bonded with steel during weld overlaying.
The Tungsten Carbide volume rate in 60%W2C-WC+40%NiBSi is about 43%. The abrasion resistance of T43 is very good and close to 60%W2C-WC+40%NiBSi. T43E43 is Ferro Matrix super wear resist up to 900℃ for Gas Valve Laser or PTA Plasma Cladding in Car Industry or Hot Rolling Steel Guider. The volume price of T43 powder is very competitive only 1/10 one ten of the 60%W2C-WC+40%NiBSi for Laser or PTA Plasma cladding Conical Mining Drill Bits etc.
T35N45, T35F45, T35C40 coating is no cracking without preheating. T35C40 is super Cavitation resist in addition to good corrosion resist and very good abrasion resist for Laser or PTA Plasma Cladding Hydro Turbine Runners, Propeller Blades, Impeller Runners, Pumps etc.
T43 Laser Clad Mud Pump Liner T35C for Cavitation Abrasion T79 for Cored Wire Filler
3. AMTmetalTech Unique Top Quality World Low Price FerroTiC Titanium Carbide Hardface Deposit Powders Replace Nickel Tungsten Carbide Laser / PTA Plasma Overlay Cladding or Cored Wire Filler Advantages
FerroTiC Advantages | FerroTiC, T79F20 | Pure TiC |
Density | about 5.8 | 4.93 |
TiC Grain Size | 1-2um | 53-150um |
Coating Homogeneity | Homogenious for T79F20 is dissolved to be fine TiC | Less Homogenious for Thick TiC easy to float |
Coating Brittleness | Less Brittle for fine TiC already bonded with Steel | More Brittle for pure thick TiC |
Bonding after Cladding | Better bonding for fine TiC already bonded with Steel during vacuum sintering before cladding | Pure thick TiC is easy to be oxidized and less easy to be bonded with Steel during cladding |
Cracking Tendency of Coating | Less Cracking Tendency | More Cracking Tendency |
TiC content rate allowed in coating to prevent cracking | Higher | Less |
4. AMTmetalTech Unique Top Quality World Low Price FerroTiC Titanium Carbide Steel Cemented Hardmetal Wear Parts
The wear resistance of AMTmetalTech Unique Titanium Carbide Hardmetal is as Ferro-Titanit & close to Tungsten Carbide Hardmetal. The volume price is much lower than Tungsten carbide Hardmetal for the Low density.
Type | TiC, wt% | Density, g/Cm3, min. | Typical Hardness, HRA | Bend Strength, MPa, min. | Porosity | Impact, J/Cm3, min. | Description | Properties | Applications |
MT-316LTiC50 | 50 | 6.0 | 86 | 1800 | 316L Titanium Carbide Hardmetal with 316L matrix | 1、High hardness and good corrosion resist. | Mainly for Wear Parts and Crusher inserts.
| ||
MT-316LTiC60 | 60 | 5.7 | 88 | 1500 | |||||
MT17-4TiC50 | 50 | 6.0 | HRC50 Sintered, HRC68 Quenched | 2300 | 17-4 Titanium Carbide Hardmetal with 17-4 matrix | ||||
MT-HMTiC50 | 50 | 6.0 | 85.0 | 2800 | A04B00 | 13 | Titanium Carbide HardmetaL with High Manganese Steel matrix similar as Ferro-Titanit. | 1、High hardness and Good toughness. | Mainly for Mining Inserts and Bits.
|
MT-HMTiC54 | 54 | 5.9 | 86.0 | 2600 | A04B00 | 12 | |||
MT-HMTiC56 | 56 | 5.8 | 87.0 | 2400 | A04B00 | 12 | |||
MT-HMTiC59 | 59 | 5.7 | 88.0 | 2200 | A04B00 | 10 | |||
MT-HMTiC63 | 63 | 5.6 | 88.5 | 1800 | A04B00 | 10 | |||
MT-HMTiC67 | 67 | 5.5 | 89.0 | 1800 | A04B02 | 10 | |||
MT-HMTiC72 | 72 | 5.4 | 90.0 | 1800 | A04B02 | 9 | |||
MT-STTiC35 | 35 | 6.5 | HRC57 Sintered, Annealed, Quenched | 2200 | A04B00 | 5.9 | Titanium Carbide HardmetaL with tool steel matrix similar as Ferro-Titanit. | 1、High hardness and Good toughness. | Mainly for Cutters and Moulds.
|
Please send us email to export@AMTmetalTech.com about FerroTiC Titanium Carbide for HS-LMD Laser Deposit Euro7 Brake Disc or Conical Mining Bit Hardface, LaNi5 AB5 / TiMn2 AB2 / TiFe AB Hydrogen Storage Alloy, HDH Hydride-dehydride Titanium Ti64 Powder Sintered Billet Forge Superior than HIP Hot Isostatic Pressing, Gas Atomized Powder Bed Fusion / PM / MIM / SLS / SLM / Binder Jetting Ceramic 3D Printed Copper / Cobalt / Vehicle or Automobile Car Gear, Raney Nickel Aluminum NiAlMo Mesh Cathode Catalyst of Electrolysis Hydrogeneration Fibre Felt / Hastelloy / Inconel In625 / Stellite / MCrAlY / CoNiCrAlY / NiCoCrAlY / Ti 6Al 4V / Duplex Stainless Steel & 316L or Agglomerated Sintered WC-10Co-4Cr / WC-12Co / Cr3C2-NiCr / Moly Powder for HVAF / HVOF Thermal or Cold Spraying or PTA Clad Weld Overlay Elbow, Cast or Fused Tungsten Carbide Brazing Rope, Hafnium Zirconium Wires / Rods for Plasma Cutting from Crystal Iodide Hafnium Bar, Tantalum Ta & Niobium Nb for Alloy Melting or Foil / Target / Sheet Welding, Molybdenum Lanthana MoLa Filament EDM Wire, Amorphous Fine Powder Tube Inside ID Spraying replacing Chrome Plating for severe Erosion Cavitation high temperature abrasion resist of Stirrer Blade / Hydro Turbine Runner / Electronics; Hardmetal Cemented Clad Mud Pump Liner / Pipe / Tile / Super Wear Plate; PDC Diffusion Bonding, Diamond Bearing etc.